A composite Pd coated electrode was prepared, which was modified with polypyrrole (PPy) and multiwall carbon nanotubes (MWCNTs), named Pd/PPy-MWCNTs/Ti electrode. The preparation parameters of Pd/PPy-MWCNTs/Ti were discussed. The content of MWCNTs adsorbed on Ti substrate was 1.0 mg, the polymerization current of pyrrole was 5 mA for 4 min and the depositing current of Pd was 40 mA for 45 min. The prepared electrode was characterized by scanning electron microscopy (SEM) and X-ray diffraction (XRD). It was used for pentachlorophenol (PCP) dechlorination in aqueous solution. PCP with initial concentration of 10 mg/L was completely removed by Pd/PPy-MWCNTs/Ti electrode in 90 min under the conditions of the electrolysis current of 5 mA and the initial pH of 2.2 at ambient temperature. The removal of PCP was maintained at 100% when Pd/PPy-MWCNTs/Ti electrode was reused eight times. It revealed that the self-made electrode had good stability for electrochemical dechlorination.