Rubrene　thin　films　are　deposited　on　quartz　substrates　and　silver　nanoparticles　(Ag　NPs)　films　by　the　thermal　evaporation　technique.　The　optical　properties　of　rubrene　thin　film　are　investigated　in　a　spectral　range　of　190　nm-1600　nm.　The　analysis　of　the　absorption　coefficient　(alpha)　reveals　direct　allowed　transition　with　a　corresponding　energy　of　2.24　eV.　The　photoluminescence　(PL)　peak　of　the　rubrene　thin　film　is　observed　to　be　at　563　nm　(2.21　eV).　With　the　use　of　Ag　NPs　which　are　fabricated　by　radio-frequency　(RF)　magnetron　sputtering　on　the　quartz,　the　PL　intensity　is　8.5　times　that　of　as-deposited　rubrene　thin　film.　It　is　attributed　to　the　fact　that　the　surface　plasmon　enhances　the　photoluminescence.