We　annealed　Ge-Sb-S-CsCl　glass　and　investigated　the　evolution　of　the　structural,　optical　and　mechanical　properties　as　a　function　of　annealing　temperature.　It　was　found　that,　for　the　glass　annealed　at　280　degrees　C　for　210　h,　a　CsCl　crystalline　phase　with　mono-dispersedly　spherical　shape　was　formed;　while　for　the　glass　annealed　at　370　degrees　C　for　5　h,　both　beta-GeS2　and　CsCl　crystalline　phases　with　irregular　distribution　of　large　grains　was　observed.　While　the　density　and　the　microhardness　of　the　glasses　increase　with　increasing　annealing　temperature,　it　was　found　that,　optical　loss　in　the　glass　annealed　at　370　degrees　C　for　5　h　was　much　larger　than　that　annealed　at　280　degrees　C　for　210　h.　(C)　2014　Elsevier　B.V.　All　rights　reserved.