Li4Ti5O12　thin　film　electrodes　are　successfully　deposited　on　Pt/Ti/SiO2/Si　substrates　by　pulsed　laser　deposition　(PLD)　technique.　The　microstructure　and　morphology　of　Li4Ti5O12　thin　films　are　characterized　by　XRD　and　ESEM.　The　electrochemical　properties　of　Li4Ti5O12　thin　film　electrodes　are　evaluated　by　galvanostatic　cycling　test.　The　kinetic　behavior　of　lithium　ions　in　Li4Ti5O12　thin　film　electrodes　is　also　conducted　using　cyclic　voltammetry　(CV),　galvanostatic　intermittent　titration　technique　(GITT),　and　electrochemical　impedance　spectroscopy　(EIS).　Li4Ti5O12　thin　film　electrodes　show　favorable　specific　capacities　and　cycle　performance.　The　chemical　diffusion　coefficients　are　found　to　be　in　a　range　of　10(-15)　to　10(-12)　cm(2)　s(-1)　determined　by　GITT　method.　The　kinetic　parameters　obtained　from　impedance　spectra　as　a　function　of　the　cell　voltage　are　investigated　in　details.　The　decrease　of　the　charge-transfer　resistance　(R-ct)　can　be　explained　by　the　two-phase　transition　during　lithium　insertion　into　Li4Ti5O12.　(C)　2014　Elsevier　B.V.　All　rights　reserved.