Magnetic　properties　and　magnetocaloric　effect　(MCE)　in　LaFe11.5Si1.5　B　(0.2)　have　been　investigated　by　substituting　30　%　Pr　for　La.　It　is　found　that　the　substitution　of　30　%　Pr　for　La　leads　to　a　reduction　in　Curie　temperature　(T　(C))　from　200　to　190　K.　The　characteristic　of　the　itinerant　electron　metamagnetic　(IEM)　transition　above　T　(C)　becomes　more　prominent　with　the　substitution　of　30　%　Pr　for　La.　The　maximum　magnetic　entropy　change　(-Delta　S　(M))　is　remarkably　enhanced　from　13.0　to　17.9　J/kg　center　dot　K　under　a　field　change　of　0-3　T,　and　correspondingly,　the　values　of　refrigerant　capacity　(RC)　for　LaFe11.5Si1.5　B　(0.2)　and　La0.7Pr0.3Fe11.5Si1.5　B　(0.2)　are　167　and　224　J/kg,　respectively.　The　large　-Delta　S　(M)　and　the　high　RC　in　a　low　magnetic　field　indicate　that　La0.7Pr0.3Fe11.5Si1.5　B　(0.2)　may　be　a　promising　candidate　for　magnetic　refrigeration　material　near　200　K.