In　this　study,　the　optimum　laser　process　parameter　was　determined　by　fatigue　experiment　for　the　treated　copper　film　specimens　with　thickness　of　25　mu　m.　The　mechanism　of　healing　fatigue　damage　was　analyzed　by　the　numerical　simulation　of　temperature　field　induced　by　laser　irradiation　and　the　microstructure　changes　on　the　surface　of　specimens.　The　results　showed　that　the　fatigue　damage　of　copper　film　specimens　can　be　healed　when　the　applied　energy　density　is　in　the　range　from　4x10(3)　J/m(2)　to　14x10(3)　J/m(2),　and　the　fatigue　life　can　increase　by　about　5　times　when　the　applied　energy　density　is　7x10(3)　J/m(2).　The　process　hardening　and　grain　refinement　in　the　surface　layer　are　mainly　responsible　for　extending　fatigue　life.