The　interface　characteristics　and　corrosion　behaviour　of　oriented　Fe2B　in　liquid　zinc　have　been　investigated.　The　results　indicate　that　Fe2B　with　preferential　growth　direction　parallel　to　corrosion　interface　displays　better　corrosion　resistance　to　liquid　zinc.　The　Fe2B/FeB　phase　transition　occurs　due　to　gradient　of　chemical　potential　in　solid　Fe2B-liuqid　zinc　system.　The　liquid　zinc　corrosion　is　competition　process　of　dissolution,　Fe2B/FeB　transition　and　fracture-spalling.　The　fracture-spalling　dominates　corrosion　process　when　preferred　direction　of　Fe2B　is　perpendicular　to　corrosion　interface　while　Fe2B/FeB　transition　plays　a　role　in　liquid　zinc　corrosion　as　preferred　direction　of　Fe2B　is　parallel　to　corrosion　interface.　Crown　Copyright　(C)　2013　Published　by　Elsevier　Ltd.　All　rights　reserved.