摘要:
A Ni-5at%W ingot was prepared by medium frequency induction melting. The ingot was forged, hot-rolled and cold-rolled into trips with 60 mu m thickness and 50 m length. Recrystallization annealing for the substrate trip was carried out at different temperatures (800 similar to 1200 degrees C) for different time. Taking account of high cube texture and shallow boundary, the recrystallization annealing of 1100 degrees C/0.5 h is regarded as the best. According to X-ray diffraction and EBSD analyses, the cube grain content of the tape annealed at 1100 degrees C for 0.5 h reaches as high as 98.9% (tolerance angle of less than 10 degrees), and grain size is uniform. The FWHM values of the in-plane and the content of crystal twin are slightly different from that of the commercial Ni5W tape supplied by Germany Dresden.