The fatigue behaviour of nickel-based GH4169 alloy was studied under multiaxial loading at 650 degrees C. During the middle and late stages of the fatigue life at 650 degrees C, the axial and shear maximum stresses continue to decrease and plastic strains continue to increase, while at 360 degrees C different phenomena are observed. The intergranular cracks and certain quantities oxygen were observed in the fracture surfaces. The damage of creep and oxidation are related to temperature and strain range. The life prediction results with a time-dependent fatigue damage model show the time-related factors have a certain influence on the fatigue damage.