The　Sr3Y1-x(PO4)(3):xDy(3+)　powder　samples　were　synthesized　by　solid-state　reaction　method.　The　PL　and　PLE　spectra　showed　that　the　phosphor　could　be　excited　by　light　from　350　to　460　nm　and　two　strong.　peaks　centered　at　484　nm　and　576　nm　corresponding　to　the　magnetic　dipole　F-4(9/2)　-＞　H-6(15/2)　transition　and　the　electric　dipole　F-4(9/2)　-＞　H-6(13/2)　transition.　According　to　the　Dexter＇s　theory,　it　was　found　that　the　major　mechanism　for　concentration　quenching　as　a　result　of　dipole-dipole　(d-d)　interaction.　The　chromaticity　coordinates　of　Sr3Y1-x(PO4)(3):xDy(3+)　phosphors　are　close　to　the　white　color　chromaticity　coordinates　(x=0.33,　y=0.33).　These　results　indicate　that　the　Sr3Y1-x(PO4)(3):xDy(3+)　phosphor　may　be　a　promising　single-component　phosphor　in　the　field　of　white　LEDs.　(C)　2013　Elsevier　B.V.　All　rights　reserved.