The　microstructural　evolution　of　Ti-45　center　dot　9Al-8Nb　and　Ti-45　center　dot　9Al-8Nb-0　center　dot　2C　(at-%)　alloys　fabricated　by　centrifugal　investment　casting　is　studied.　It　is　found　that　both　Ti-45　center　dot　9Al-8Nb　and　Ti-45　center　dot　9Al8Nb-0　center　dot　2C　are　mainly　composed　of　gamma　phase　and　a　small　amount　of　alpha(2)　phase,　and　the　microstructure　is　mainly　fully　lamellar　in　C　containing　alloy　but　again　the　C　free　alloy　is　mainly　nearly　fully　lamellar.　Nb　distributes　homogeneously　in　the　gamma　and　alpha(2)　phases　but　is　depleted　in　the　interdendritic　regions.　The　addition　of　C　reduces　the　lamellar　spacing　of　Ti-45　center　dot　9Al-8Nb　alloy.　The　mean　interlamellar　spacings　between　alpha(2)　and　alpha(2)　of　Ti-45　center　dot　9Al-8Nb　and　Ti-45　center　dot　9Al-8Nb-0　center　dot　2C　alloys　are　about　950　and　700　nm,　and　those　between　gamma　and　alpha(2)　lamellae　are　about　320　and　220　nm　respectively.　Oil　cooling　from　the　a　phase　field　after　1h　treatment　at　1360　degrees　C　leads　to　massive　transformation　to　gamma(m)　for　both　Ti-45　center　dot　9Al-8Nb　and　Ti-45　center　dot　9Al-8Nb-0　center　dot　2C　alloys.　Subsequent　aging　in　the　azc　phase　field　results　in　a　phase　precipitates　within　the　gamma(m)　phase,　which　leads　to　convoluted　microstructures.　However,　the　C　addition　retards　the　precipitation　of　alpha(2)　phase.