Ternary system ceramic 0.2Pb(Zn1/3Nb2/3)O-3-0.8Pb(Zr-0.5,Ti-0.5)O-3(1-x)(Ni51.5Mn25Ga23.5)x prepared by solid state reaction were investigated. The test methods such as XRD test and VSM test were applied to analyze its properties and structure. X-ray diffraction (XRD) indicates that Ni51.5Mn25Ga23.5 has all soluted into 0.2Pb(Zn1/3Nb2/3)O-3-0.8Pb(Zr-0.5,Ti-0.5)O-3 lattice first and then Ni51.5Mn25Ga23.5 exists in composite system by separate phase. Thus it makes the diffraction peaks shift to right. Ferroelectric tests show that remanent polarization is decreased with x increasing and coercive field is first decreased and then increased. The magnetic field dependence of magnetization indicates remanent magnetization increasing with x increasing.