Using　in　situ　x-ray　diffraction,　we　demonstrate　a　pressure-induced　crystallization　of　as-deposited　amorphous　Ge2Sb2Te5　(a-GST)　into　a　body-centered-cubic　(bcc)　solid　solution　at　28　GPa,　and　the　back　transformation　from　the　bcc-GST　to　a-GST.　A　large　hysteresis　loop　was　observed,　as　the　bcc-GST　was　retained　until　15　GPa.　Comparisons　have　been　made,　employing　the　x-ray　data　and　the　structural　information　obtained　from　ab　initio　molecular　dynamics　simulations,　between　the　as-deposited　a-GST　and　the　a-GST　obtained　from　the　pressure-induced　collapse　of　the　rocksalt　GST,　both　at　a　high　hydrostatic　pressure　(20　GPa)　prior　to　their　crystallization　to　bcc.　The　results　suggest　that　both　routes　have　resulted　in　the　same　high-pressure　amorphous　state,　which　explains　their　crystallization　into　bcc-GST　at　similar　pressures.　(C)　2010　American　Institute　of　Physics.　[doi:10.1063/1.3493110]