Fine　ferroelectric　properties　with　remnant　polarization　of　22.7　mu　C/cm(2)　and　coercive　field　of　16.1　kV/cm　of　(1-x)K0.5Na0.5NbO3-xLiNbO(3)　((1-x)KNN-xLN)　ceramics　were　obtained　by　laser　sintering　method.　The　optimum　piezoelectric　properties　of　piezoelectric　constant　d(33)　similar　to　110　pC/N　do　not　exist　in　the　ceramics　with　the　amount　of　LiNbO3　at　x　=　0.06　but　lower　to　x　=　0.04.　The　texture　structure　with　the　increase　of　(001)　orientation　along　the　spontaneous　polarization　directions　results　in　strong　contribution　to　the　ferroelectric　response.　High　substitution　effect　of　Li+　leads　to　the　transformation　from　orthorhombic　phase　to　tetragonal　phases　occurring　at　lower　amount　of　LiNbO3.