In　this　study,　based　on　different　anodized　aluminium(AAO)　templates　obtained,　the　high　ordered　aligned　titania　nanoarray　thin　films　have　been　fabricated　via　liquid　phase　deposition(LPD)　method.　The　results　show　that　the　crystal　structure　of　the　titanium　oxide　nanoarray　thus　obtained　was　anatase　after　heat-treating　at　400　degrees　C　for　4　h.　The　volume　fraction　of　Al2O3　on　the　template　prepared　in　oxalic　acid　template　more　than　0.71,　the　ordered　aligned　titania　nanorods　are　synthesized,　characterized　with　the　outer　diameter　of　100　nm.　The　volume　fraction　of　Al2O3　on　the　template　prepared　in　phosphoric　acid　template　less　than　0.71,　the　ordered　aligned　titania　nanotubes　are　synthesized,　characterized　with　the　outer　diameter　of　200　run　and　the　inner　diameter　of　100　nm.