In this work, we fabricate a highly efficient photocatalytic AgBr/Ag2CO3 heterojunction through the co-precipitation method. The obtained samples were characterized by means of X-ray diffraction, scanning electron microscopy, transmission electron microscopy, ultraviolet-visible diffuse reflectance spectra and X-ray photoelectron spectroscopy. The photocatalytic activities of obtained samples can be assessed by visible light (lambda >= 400 nm) degradation of rhodamine B solution. X-ray diffraction revealed that the crystallinity of the AgBr/Ag2CO3 heterojunction was significantly higher than pure AgBr and Ag2CO3. Moreover, the AgBr/Ag2CO3 heterojunction prepared at pH = 6 has the best photocatalytic performance, it can raise the degradation degree of rhodamine B over 95% at 20 min. Finally, a possible photocatalytic mechanism is discussed.
关键词:
通讯作者信息:
来源 :
INTERNATIONAL JOURNAL OF MATERIALS RESEARCH
ISSN: 1862-5282
年份: 2020
期: 10
卷: 111
页码: 842-848
0 . 8 0 0
JCR@2022
ESI学科: MATERIALS SCIENCE;
ESI高被引阀值:37
JCR分区:4