Titania　of　different　crystalline　structures　and　morphology　was　prepared　by　the　low　temperature　dissolution-reprecipitation　process　(LTDRP)　of　amorphous　precursors　in　various　acidic　mediums　at　70　degrees　C　for　8　h.　The　effects　of　different　acids　on　the　crystalline　and　morphology　of　titania　nanostructures　were　investigated　by　X-ray　diffraction　(XRD)　and　transmission　electron　microscopy　(TEM).　Results　showed　that　HCl,　HNO3　and　their　mixture　favored　the　formation　of　rod-like　rutile　TiO2,　while　H2SO4　and　its　mixture　with　HCl　or　HNO3　retarded　the　formation　of　rutile　but　favored　the　formation　of　the　anatase　phase　of　with　an　irregular　shape.　The　mechanism　of　the　formation　of　various　titania　nanostructures　was　also　discussed.　(C)　2008　Published　by　Elsevier　B.V.