A　new　calcium　borate,　CaB6O10,　has　been　prepared　by　solid-state　reactions　at　temperature　below　750　degrees　C.　The　single-crystal　X-ray　structural　analysis　showed　that　CaB6O10　crystallizes　in　the　monoclinic　space　group　P2(l/c)　with　a=9.799(1)angstrom,　b=8.705(1)angstrom,　c=9.067(1)angstrom,　beta=116.65(1)degrees,　Z=4.　It　represents　a　new　structure　type　in　which　two　[B3O7](5-)　triborate　groups　are　bridged　by　one　oxygen　atom　to　form　a　[B6O13](8-)　group　that　is　further　condensed　into　a　3D(infinity)(3)[B6O10](2-)　network.　with　the　shorthand　notation　6:　infinity(3)[2　x　(3:2　Delta　+　T)].　The　3D(infinity)(3)[B6O10](2-)　network　affords　intersecting　open　channels　running　parallel　to　three　crystallographically　axis　directions,　where　Ca2+　cations　reside.　The　IR　spectrum　further　confirms　the　presence　of　both　BO3　and　BO4　groups　(C)　2007　Elsevier　B.V.　All　rights　reserved.