The　YBCO　films　were　directly　deposited　on　the　{110}　＜　0　11　＞　textured　Ag　substrates　by　ultrasonic　spray　pyrolysis　method.　The　observed　white　points　in　YBCO　film　by　one-step　deposition　at　900　degrees　C　consisted　in　high　content　of　Ag　on　the　surface　of　this　film,　which　was　due　to　the　evaporation　and　diffusion　of　Ag　atoms　at　high　deposition　temperature.　While　the　performance　of　YBCO　films　was　significantly　enhanced　using　two-step　deposition　route.　A　15　cm　length　of　coated　YBCO　film　on　{110}　＜　0　11　＞　textured　Ag　tape　was　prepared　by　this　two-step　deposition　method,　which　exhibited　a　transport　J(c)　value　of　more　than　10(4)　A/cm(2)　(at　77　K).　(c)　2007　Elsevier　B.V.　All　rights　reserved.