A　kind　of　lead-free　ferroelectric　nanorods,　(K0.5Bi0.5)(0.4)Ba0.6TiO3,　has　been　prepared　by　the　sol-gel　process.　The　phase　formation,　structure　and　morphological　analyses　of　(K0.5Bi0.5)(0.4)Ba0.6TiO3　were　investigated　by　XRD,　FTIR,　Raman　and　TEM.　The　results　revealed　that　single-crystalline　(K0.5Bi0.5)(0.4)Ba0.6TiO3　nanorods　with　width　around　80　to　120　nm,　and　length　around　200-300　nm　were　obtained　by　calcining　dried　gels　at　800　degrees　C　for　2　h.　Raman　analysis　of　(K0.5Bi0.5)(0.4)Ba0.6TiO3　nanorods　indicated　that　A(1)　(TO2)　and　E(TO)　mode　incorporated　into　one　broad　peak　at　around　285　cm(-1),　which　can　be　attributed　to　the　cation　disorder　(Bi,　K,　Ba)　on　the　12-fold　coordinated　A　site　of　ABO(3)　structure.　(C)　2006　Elsevier　B.V.　All　rights　reserved.