The　YBCO　films　were　directly　deposited　on　the　{110}　＜　011　＞　textured　Ag　substrates　by　an　ultrasonic　spray　pyrolysis　method　using　the　modified　device.　The　YBCO　film　made　by　one-step　deposition　at　900　degrees　C　on　textured　Ag　substrate　has　a　weak　in-plane　texture　and　low　J(c)　value.　The　observed　white　points　in　this　film　consist　of　high　content　of　Ag　on　the　surface　of.　this　film,　which　are　due　to　the　vaporization　and　diffusion　of　Ag　atoms　at　high　deposition　temperatures.　While　the　performance　of　YBCO　films　can　be　significantly　enhanced　by　using　two-step　deposition　route,　firstly　pre-depositing　the　precursor　film　at　700　degrees　C　then　carrying　out　the　second　step　depositing　at　900　degrees　C.　The　results　show　that　the　two-step　deposition　can　effectively　prevent　Ag　atoms　from　vaporizing　and　diffusing　into　YBCO　films　and　improve　the　surface　roughness,　texture　and　superconducting　properties　of　YBCO　films.　The　YBCO　film　being　15cm　long,　coated　on　{101}＜　011　＞　textured　Ag　tape　by　this　two-step　deposition　method　exhibits　a　transport　J,　value　of　more　than　10(4)A/cm(2)　at　77K.