A　mild　hydrothermal　method　has　been　adopted　to　prepare　La1-xSrxMnO3　(x　=　0.33,　0.5,　0.6　and　0.75),　which　is　of　interest　for　a　number　of　possible　applications,　for　example　the　colossal　magneto　resistance　(CMR).　The　results　from　X-ray　diffraction　(XRD)　indicate　that　pure　phases　La1-xSrxMnO3　have　been　prepared　at　240　degrees　C.　Furthermore,　the　synthesis　yields　clearly　faceted　cubes　with　a　cubic　perovskite　structure.　Typical　cubes　have　rising　sizes　ranging　between　2　and　10　mu　m　with　the　strontium　doping　level　rising.　Fourier　transform　infrared　(FTIR)　spectroscopy　performed　on　La1-xSrxMnO3　shows　that　there　is　little　difference　in　these　samples　with　different　doping　levels.　(c)　2006　Elsevier　B.V.　All　rights　reserved.