A　kind　of　novel　lead-free　ferroelectrics,　potassium　bismuth　titanate,　K0.5Bi0.5TiO3　(KBT),　has　been　prepared　by　sol-gel-hydrothermal　and　sol-gel　routes,　respectively,　and　the　structural　characters　of　as-synthesized　powders　were　characterized　by　X-ray　diffraction　(XRD),　transmission　electron　microscopy　(TEM)　and　scanning　electron　microscopy　(SEM).　The　results　indicated　that　sol-gel-hydrothermal　route　led　to　the　formation　of　KBT　nanowhiskers　with　diameters　of　20　nm　and　lengths　of　1　mu　m,　and　the　processing　temperature　was　as　low　as　160　degrees　C,　but　the　normal　sol-gel　route　tended　to　form　KBT　cubic　particles　of　about　100-200　nm　and　the　processing　temperature　was　higher　than　700　degrees　C.　It　is　believed　that　the　gel　precursor　and　hydrothermal　environment　play　an　important　role　in　the　formation　of　the　nanowhiskers　at　low　temperature.　Due　to　the　＇good　sinterability　of　nanowhiskers,　the　ferroelectric　and　dielectric　properties　of　KBT　ceramics　prepared　by　sol-gel-hydrothermal　route　were　super　to　that　prepared　by　sol-gel　route.　(c)　2006　Elsevier　Ltd.　All　rights　reserved.