Using　mobium-chelated　precursor,　a　novel　method　for　synthesizing　layered　niobate　(K4Nb6O17)　thin　films　was　developed.　After　annealing　at　600　degrees　C　or　above,　the　nanostructured　K4Nb6O17　thin　films　with　(040)　preferred　orientation　were　successfully　produced　by　sol-gel　process.　XPS　measurement　showed　that　the　atomic　ratio　of　K:Nb:O　in　the　thin　film　was　4.08:5.99:16.77,　which　was　in　good　accordance　with　the　stoichiometry　of　K4Nb6O17,　Varying　with　annealing　parameters,　the　layered　structure　of　the　thin　films　altered　and　the　hydrated　layered　K4Nb6O17　center　dot　3H(2)O　thin　films　presented　while　low　pyrolysis　temperature　was　applied.　The　hydrogen　evolution　from　water　decomposition　showed　the　excellent　photocatalytic　properties　of　the　films.　The　static　hydrogen　evolution　for　the　thin　film　annealed　at　600　degrees　C　reached　105　mu　mol　cm(-2)　h(-1).　(c)　2005　Elsevier　B.V.　All　rights　reserved.