Complicate　preparing　procedure　of　ultrahigh　carbon　steels　(UHCSs)　greatly　limited　their　practical　application　in　industry.　In　the　course　of　searching　a　simple　method　for　the　preparation　of　the　ultrahigh　carbon　steels,　we　found　a　fully　fine　pearlite　microstructure　formed　in　the　Al-added　steel　with　high　carbon　content.　Our　results　proved　that　the　steel　can　be　directly　spheroidized　into　uniformly　distributed　fine　carbides,　and　that　the　steel　with　fine　spherodized　carbides　showed　high　tensile　strength　of　1010　MPa　and　high　yielding　strength　of　650　MPa,　together　with　good　elongation　of　12.8%.　(C)　2005　Elsevier　B.V.　All　rights　reserved.