Ca2Co2O5　textured　ceramics　were　rapidly　prepared　by　a　coprecipitation　method　and　spark　plasma　sintering　(SPS)　using　cobalt　and　calcium　nitrates　as　starting　materials　and　sodium　hydroxide　as　precipitant.　Single　phase　Ca2Co2O5　ceramics　can　be　obtained　by　SPS　at　800　degrees　C　for　5　min　using　the　precursor　powders　calcined　at　700-850　degrees　C　for　2　h.　It　is　critical　to　obtain　stochiometric　precursor　by　controlling　the　final　pH　13.2　during　the　coprecipitation　process.　The　SPS　process　is　effective　in　obtaining　single　phase　Ca2Co2O5　ceramics.　The　thermoelectric　properties　of　the　prepared　sample　were　investigated　from　100　to　700　degrees　C.　At　700　degrees　C,　the　electrical　resistivity,　Seebeck　coefficient,　thermal　conductivity　and　figure　of　merit　of　the　sample　are　9.30　x　10(-5)　Omega　m,　178　mu　V/K,　1.55　W/mK　and　0.21,　respectively.　(c)　2005　Elsevier　B.V.　All　rights　reserved.