Mechanochemical　reaction　method　was　used　for　preparing　fluorine-doped　SrTiO3　and　the　influences　of　several　parameters　on　the　visible　light　photocatalysis　of　the　samples　were　studied.　In　the　samples　of　5　mol%　SrF2-SrTiO3　ground　for　10-240　min,　the　sample　ground　for　60　min　showed　the　highest　capability　for　the　elimination　of　NO.　The　postgrinding　heat　treatment　at　appropriate　temperature　(150-200degreesC)　in　air　could　improve　the　photo-oxidation　capability　of　fluorine-doped　SrTiO3　probably　due　to　the　decrease　in　the　number　of　hydroxyl　groups　on　the　surface　of　the　powder　in　the　sample.　The　samples　made　by　1　-　5　mol%　SrF2　-　SrTiO3　mixtures　showed　high　photocatalytic　activity,　whereas　excess　content　of　SrF2　resulted　in　decreasing　activity　due　to　the　formation　of　a　new　fluoride　compound　in　the　sample.　The　sample　prepared　by　grinding　the　mixture　of　5　mol%　SrF2　and　95　mol%　SrTiO3　for　I　h　followed　by　heat　treatment　at　150degreesC　for　2　h　showed　about　three　and　two　times　larger　photocatalytic　activity　for　the　elimination　of　NO　under　the　irradiation　of　visible　light　(wavelength　＞　510　nm)　than　pure　SrTiO3　and　P-25,　respectively.　(C)　2004　Elsevier　B.V.　All　rights　reserved.