Nitrogen　doped　SrTiO3　powders　were　prepared　by　the　mechanochemical　reaction　of　SrTiO3　and　20　wt.%　of　three　kinds　of　doping　sources,　hexamethylenetetramine,　urea,　and　ammonium　carbonate　using　a　high　energy　planetary　ball　mill,　followed　by　calcination　at　400　degreesC　for　1　h.　The　photocatalysis　of　nitrogen　doped　SrTiO3　powders　under　the　irradiation　of　wavelength　lambda　＞　400　nm　and　near　ultraviolet　light　regions　(lambda　＞　290　nm)　greatly　changed　depending　on　particle　size,　specific　surface　area　and　porosity.　The　absorption　of　visible　light　increased　with　increasing　nitrogen　content　doped　in　SrTiO3　lattice.　Nitrogen　monoxide　elimination　ability　of　SrTiO3　could　be　greatly　improved　by　nitrogen　doping.　The　photocatalytic　activity　of　nitrogen　doped　SrTiO3　made　by　20　wt.%　hexamethylenetetramine-SrTiO3　under　light　lambda　＞　400　nm　irradiation　was　about　3.5　and　1.4　times　higher　than　those　of　pure　SrTiO3　and　commercial　titania　powder　(Degussa　P-25).　(C)　2004　Elsevier　B.V.　All　rights　reserved.