The　development　of　a　new　piezoelectric　material,　0.5.wt.%MnO2-addcd　(Pb0.95Sr0.05)((Zn1/3Nb2/3)(0.20)(Zr0.50Ti0.50)(0.80))O-3　Ceramics　(PZNST),　optimized　for　use　in　multilayer　piezoelectric　transformer　application　is　described.　The　requirements　to　such　a　material　are　high　mechanical　quality　factor　of　Q(m),　electromechanical　coupling　factor　of　k(p),　Curie　temperature　of　T-c　and　low　dielectric　dissipation　factor　of　tandelta,　and　at　the　same　time　a　relative　low　sintering　temperature.　The　dielectric　and　piezoelectric　properties　of　the　new　developed　material,　PZNST,　have　been　investigated　on　different　sintering　temperature　(900-1100　degreesC).　The　pure　perovskite　phase　was　formed　by　the　columbite　precursor　method.　The　optimum　values　of　Q(m),　k(p),　tandelta,　epsilon(r),　T-c　and　d(33)　were　1360,　0.62,　0.002,　1240,　320　degreesC　and　325　pC/N,　respectively,　at　calcination　of　850　degreesC　and　sintering　of　1000　degreesC　temperature.　(C)　2003　Elsevier　B.V.　All　rights　reserved.