A　new　strategy　to　chemically　synthesize　exchange-coupled　SmCo5/Sm2Co17　nanocomposites　by　in　situ　decomposition　of　SmCox(5　＜　x　＜　8.5)　is　reported　in　this　work.　Our　synthesis　starts　with　the　fabrication　of　Co/Sm2O3　(Sm　to　Co　atomic　ratio　of　Sm/Co　=　1:4.2),　which　can　be　reduced　into　40-nm　SmCo5　single　crystal　nanoparticles　by　Ca　under　the　protection　of　CaO,　showing　a　high　coercivity　of　2.85　T　and　saturation　magnetization　(M-s)　of　0.0671　A.m(2).g(-1).　By　changing　the　Sm/Co　to　1:4.5,　1:4.8　and　1:5.2,　SmCo5/Sm2Co17　nanocomposites　with　different　proportions　were　acquired　using　the　same　process.　Owing　to　the　in　situ　decomposition　of　SmCox　intermediate,　the　small　size　(both　of　their　size　less　than　10　nm)　and　uniform　phase　distribution　were　achieved　in　our　nanocomposites.　Thus,　the　as-prepared　nanocomposites　display　a　strong　exchange-coupling　interaction.　As　a　consequence,　SmCo5/Sm2Co17(Sm/Co　=　1:5.2)　exhibits　a　coercivity　of　1.23　T　and　enhanced　M-7T(magnetization　at　7　T)　of　0.0812　A.m(2).g(-1),　increasing　by　21%　than　pure　SmCo5.　Our　synthesis　provides　a　new　protocol　to　prepare　exchange-coupled　high-performance　nanocomposites.