Study on Intermediate Frequency Spot Welding Process of Hot Stamping High Strength Steel - 文章详情页

作者：

Yu, Yang (Yu, Yang.) | Wang, Chao (Wang, Chao.) | Chen, Shujun (Chen, Shujun.) (学者：陈树君) | Lu, Zhenyang (Lu, Zhenyang.)

收录：

CPCI-S EI Scopus

摘要：

The　joints　of　RSW　for　HSHSS　were　prepared　with　IF　spot　weld　equipment.　The　weld　nugget,　fracture　mode,　microstructure　and　micro-hardness　of　the　joints　were　investigated.　The　weld　nugget　increases　and　the　fracture　mode　changes　from　interfacial　fracture　to　nugget　plug　fracture　with　the　increasing　welding　current.　There　are　three　distinct　zones　in　the　weld　joint:　weld　nugget,　heat　affected　zone　(HAZ)　and　base　metal.　The　microstructure　of　HAZ　includes　tempered　zone　(HAZ-1),　incomplete　quenching　zone　(HAZ-2)　and　complete　quenching　zone　(HAZ-3).　The　micro-hardness　of　weld　nugget　and　HAZ-3　is　same　with　the　base　metal.　The　micro-hardness　of　HAZ-1　and　HAZ-2　is　smaller　than　that　of　base　metal.

关键词：

Intermediate frequency (IF) Hot stamping high strength steel (HSHSS) Resistance spot welding (RSW)

作者机构：

[ 1 ] [Yu, Yang]Beijing Univ Technol, Adv Mfg Technol Automot Struct Components Engn Ct, Educ Minist, Beijing 100124, Peoples R China
[ 2 ] [Wang, Chao]Beijing Univ Technol, Adv Mfg Technol Automot Struct Components Engn Ct, Educ Minist, Beijing 100124, Peoples R China
[ 3 ] [Chen, Shujun]Beijing Univ Technol, Adv Mfg Technol Automot Struct Components Engn Ct, Educ Minist, Beijing 100124, Peoples R China
[ 4 ] [Lu, Zhenyang]Beijing Univ Technol, Adv Mfg Technol Automot Struct Components Engn Ct, Educ Minist, Beijing 100124, Peoples R China

通讯作者信息：

[Yu, Yang]Beijing Univ Technol, Adv Mfg Technol Automot Struct Components Engn Ct, Educ Minist, Beijing 100124, Peoples R China

电子邮件地址：

yuy@bjut.edu.cn |
wangchao19861026@126.com |
sjchen@bjut.edu.cn |
lzy@bjut.edu.cn

查看成果更多字段

成果类型
所属机构

所有年份指定年份从至