A　series　of　three-dimensionally　ordered　macroporous　(3DOM)　nickel-copper　mixed　oxides　(with　the　NiO/CuO　molar　ratios　of　3　:　3,　3　:　2,　and　3　:　1)　calcined　at　various　temperatures　(450,　550,　and　650　degrees　C)　were　prepared　using　the　dual-templating　(Pluronic　P123　and　polymethyl　methacrylate　(PMMA))　method　in　a　mixed　solution　of　ethylene　glycol　and　methanol　with　different　volumetric　ratios　(1　:　2,　1　:　1.5,　and　1　:　1).　The　sample　obtained　after　the　use　of　P123　and　PMMA　exhibited　a　much　higher　catalytic　activity　for　CO　oxidation,　over　which　a　complete　CO　conversion　was　achieved　at　138　degrees　C,　CO/O-2　volumetric　ratio　=　2　:　5,　and　space　velocity　=　60,000　mL/(g　h),　and　this　catalyst　possessed　good　stability　in　the　presence　of　water　vapor　in　the　feed　stream.　The　large　surface　area,　high　oxygen　adspecies　concentration,　good　low-temperature　reducibility,　and　unique　nanovoid　3DOM　structure　were　accountable　for　the　superior　catalytic　performance　of　the　sample　prepared　by　the　dual　P123-　and　PMMA-templating　method.