Wu, Xinyu (Wu, Xinyu.) | Suo, Hongli (Suo, Hongli.) (学者:索红莉) | Li, Jiazhi (Li, Jiazhi.) | Ji, Yaotang (Ji, Yaotang.) | Ma, Lin (Ma, Lin.) | Liu, Min (Liu, Min.) | Dai, Yinming (Dai, Yinming.) | Liu, Jianhua (Liu, Jianhua.) | Zhang, Zili (Zhang, Zili.)

收录:

Scopus SCIE PubMed

摘要:

The microstructure and texture evolution of Ni-5 at%W (Ni5W) alloy substrates were investigated by in situ tensile testing along the rolling direction (RD), transverse direction (TD), and at 45 degrees to the RD (45 degrees-RD), as well as by electron backscatter diffraction characterization. The tensile stress direction had a significant influence on the texture evolution. The cubic texture in the Ni-5 at%W alloy exhibited severe degradation when the tensile angle was 45 degrees-RD. In contrast, the cubic texture was relatively stable under high deformation along the RD or TD. It was found that the slip line system in the 45 degrees-RD specimen was the key to the contrasting behavior. The effect of the tensile testing angle on the cubic texture evolution for Ni-W substrates was investigated, and the corresponding effect on the superconducting properties of coated materials was studied.

关键词:

cubic texture plastic deformation coated conductor electron backscatter diffraction

作者机构:

  • [ 1 ] [Wu, Xinyu]Beijing Univ Technol, Key Lab Adv Funct Mat, Minist Educ, Coll Mat Sci & Engn, 100 Pingleyuan, Beijing 100124, Peoples R China
  • [ 2 ] [Suo, Hongli]Beijing Univ Technol, Key Lab Adv Funct Mat, Minist Educ, Coll Mat Sci & Engn, 100 Pingleyuan, Beijing 100124, Peoples R China
  • [ 3 ] [Li, Jiazhi]Beijing Univ Technol, Key Lab Adv Funct Mat, Minist Educ, Coll Mat Sci & Engn, 100 Pingleyuan, Beijing 100124, Peoples R China
  • [ 4 ] [Ji, Yaotang]Beijing Univ Technol, Key Lab Adv Funct Mat, Minist Educ, Coll Mat Sci & Engn, 100 Pingleyuan, Beijing 100124, Peoples R China
  • [ 5 ] [Ma, Lin]Beijing Univ Technol, Key Lab Adv Funct Mat, Minist Educ, Coll Mat Sci & Engn, 100 Pingleyuan, Beijing 100124, Peoples R China
  • [ 6 ] [Liu, Min]Beijing Univ Technol, Key Lab Adv Funct Mat, Minist Educ, Coll Mat Sci & Engn, 100 Pingleyuan, Beijing 100124, Peoples R China
  • [ 7 ] [Dai, Yinming]Chinese Acad Sci, Inst Elect Engn, Beijing 100190, Peoples R China
  • [ 8 ] [Liu, Jianhua]Chinese Acad Sci, Inst Elect Engn, Beijing 100190, Peoples R China
  • [ 9 ] [Zhang, Zili]Chinese Acad Sci, Inst Elect Engn, Beijing 100190, Peoples R China

通讯作者信息:

  • 索红莉

    [Suo, Hongli]Beijing Univ Technol, Key Lab Adv Funct Mat, Minist Educ, Coll Mat Sci & Engn, 100 Pingleyuan, Beijing 100124, Peoples R China;;[Zhang, Zili]Chinese Acad Sci, Inst Elect Engn, Beijing 100190, Peoples R China

查看成果更多字段

相关关键词:

来源 :

MICROSCOPY AND MICROANALYSIS

ISSN: 1431-9276

年份: 2021

期: 1

卷: 27

页码: 36-43

2 . 8 0 0

JCR@2022

ESI学科: MATERIALS SCIENCE;

ESI高被引阀值:116

JCR分区:1

被引次数:

WoS核心集被引频次: 1

SCOPUS被引频次: 1

ESI高被引论文在榜: 0 展开所有

万方被引频次:

中文被引频次:

近30日浏览量: 0

归属院系:

在线人数/总访问数:406/4878616
地址:北京工业大学图书馆(北京市朝阳区平乐园100号 邮编:100124) 联系我们:010-67392185
版权所有:北京工业大学图书馆 站点建设与维护:北京爱琴海乐之技术有限公司