Hu, Mingjun (Hu, Mingjun.) | Sun, Guoqiang (Sun, Guoqiang.) | Sun, Daquan (Sun, Daquan.) | Lu, Tong (Lu, Tong.) | Ma, Jianmin (Ma, Jianmin.) | Deng, Yue (Deng, Yue.)

收录:

EI Scopus SCIE

摘要:

High viscosity modified asphalt (HVMA) is widely used as the binder for permeable asphalt pavement. The service life of permeable asphalt pavement strongly depends on the weathering aging resistance of HVMA due to the large porosity of permeable asphalt pavement. In order to investigate the accelerated deterioration effect of temperature on the weathering aging process, a laboratory accelerated weathering aging tester was used to simulate the long-term weathering aging of HVMA at different aging temperatures (30 degrees C, 50 degrees C, and 70 degrees C) and different weathering aging days (0 similar to 12d). A series of rheological tests were conducted to study the influence of weathering aging temperature on the rheological properties of HVMA. Then, FTIR test was applied to characterize the changes in chemical composition of HVMA at different weathering aging temperatures. Furthermore, an aging kinetics model was put forward to further understand the effect of aging temperature on the weathering aging rate of HVMA. The results indicate that the weathering aging rate of HVMA is fast in the early aging stage (0 similar to 2d) and slows down in the later aging stage (2 similar to 12d). The increase of aging temperature has a significant accelerated deterioration effect on the chemo-rheological properties of HVMA during weathering aging process. At 30 degrees C aging temperature, the deteriorated rheological properties of HVMA are mainly due to the aging of solar radiation. As the aging temperature increases to 50 degrees C, the thermal aging effect of HVMA begins to appear under the stimulation of solar radiation. When the aging temperature rises to 70 degrees C, HVMA has suffered from a severe coupled aging of high temperature, solar radiation and humidity. This coupled aging effect leads to a significant asphalt oxidation and polymer degradation, which is the main reason for the severely deteriorated rheological properties of HVMA. The proposed aging kinetics model results also confirm the accelerated deterioration effect of temperature during weathering aging process. (C) 2020 Elsevier Ltd. All rights reserved.

关键词:

High viscosity modified asphalt Chemical composition Rheological property Weathering aging Temperature acceleration effect Aging kinetics

作者机构:

  • [ 1 ] [Hu, Mingjun]Tongji Univ, Key Lab Rd & Traff Engn, Minist Educ, Shanghai 201804, Peoples R China
  • [ 2 ] [Sun, Daquan]Tongji Univ, Key Lab Rd & Traff Engn, Minist Educ, Shanghai 201804, Peoples R China
  • [ 3 ] [Lu, Tong]Tongji Univ, Key Lab Rd & Traff Engn, Minist Educ, Shanghai 201804, Peoples R China
  • [ 4 ] [Ma, Jianmin]Tongji Univ, Key Lab Rd & Traff Engn, Minist Educ, Shanghai 201804, Peoples R China
  • [ 5 ] [Deng, Yue]Tongji Univ, Key Lab Rd & Traff Engn, Minist Educ, Shanghai 201804, Peoples R China
  • [ 6 ] [Sun, Guoqiang]Beijing Univ Technol, Dept Rd & Railway Engn, Beijing 100124, Peoples R China

通讯作者信息:

  • [Sun, Daquan]Tongji Univ, Dept Rd & Airport Engn, 4800 Caoan Rd, Shanghai 201804, Peoples R China

电子邮件地址:

查看成果更多字段

相关关键词:

来源 :

CONSTRUCTION AND BUILDING MATERIALS

ISSN: 0950-0618

年份: 2021

卷: 268

7 . 4 0 0

JCR@2022

ESI学科: MATERIALS SCIENCE;

ESI高被引阀值:116

JCR分区:1

被引次数:

WoS核心集被引频次: 31

SCOPUS被引频次: 34

ESI高被引论文在榜: 0 展开所有

万方被引频次:

中文被引频次:

近30日浏览量: 1

归属院系:

在线人数/总访问数:478/4953959
地址:北京工业大学图书馆(北京市朝阳区平乐园100号 邮编:100124) 联系我们:010-67392185
版权所有:北京工业大学图书馆 站点建设与维护:北京爱琴海乐之技术有限公司