Membrane fouling of actual extracellular polymeric substances - 文章详情页

作者：

收录：

CPCI-S EI Scopus

摘要：

Extracellular　polymeric　substances　(EPSs)　in　activated　sludge　suspensions　are　the　key　substances　leading　to　the　membrane　fouling.　In　order　to　understand　the　effect　of　EPSs　on　the　membrane　fouling,　the　actual　EPSs　solution　extracted　from　activated　sludge　suspensions　was　used　as　the　feed　solution　to　conduct　dead-end　microfiltration　experiment　under　different　pressures　by　using　different　membranes.　The　flux　(J),　fouling　resistances　(Rm,　Rp,　Rc　and　Rtotal)　and　the　available　membrane　area　(A/A0)　were　used　to　describe　the　membrane　fouling.　The　results　showed　that　with　the　increase　of　pressure,　J　and　Rtotal　increased.　Rp　firstly　increased　and　then　kept　constant,　Rc　always　increased　and　became　the　dominant　resistance.　A/A0　decreased　from　1　to　a　constant.　Rc　plays　a　key　role　on　Rtotal　for　different　membranes　under　the　same　pressure.　The　sequence　of　the　steady　available　membrane　area　(Asteady/A0)　for　different　pressures　was:　63.0%　(0.05MPa)＞　56.5%　(0.08MPa)＞　53.6%　(0.10MPa),　and　that　for　different　membranes　was:　80.1%　(0.2μm　PES)　＞　79.9%　(0.1μm　PES)　＞　78.4%　(0.1μm　PAN)　＞　53.6%　(0.1μm　PVDF).　©　Content　from　this　work　may　be　used　under　the　terms　of　the　Creative　Commons　Attribution　3.0　licence.

关键词：

Membranes Polymers Microfiltration Energy resources Membrane fouling

作者机构：

[ 1 ] [Li, Qiang]Beijing Key Laboratory for Green Catalysis and Separation, Department of Chemistry and Chemical Engineering, Beijing University of Technology, Beijing; 100124, China
[ 2 ] [Hu, Ge]Beijing Key Laboratory for Green Catalysis and Separation, Department of Chemistry and Chemical Engineering, Beijing University of Technology, Beijing; 100124, China
[ 3 ] [Song, Peng]Beijing Key Laboratory for Green Catalysis and Separation, Department of Chemistry and Chemical Engineering, Beijing University of Technology, Beijing; 100124, China
[ 4 ] [Khaliunaa, Natsagdorj]Beijing Key Laboratory for Green Catalysis and Separation, Department of Chemistry and Chemical Engineering, Beijing University of Technology, Beijing; 100124, China
[ 5 ] [Khurram, Rooha]Beijing Key Laboratory for Green Catalysis and Separation, Department of Chemistry and Chemical Engineering, Beijing University of Technology, Beijing; 100124, China
[ 6 ] [Zhang, Hu]Beijing Fluid Filtrat and Separat Technol Res Ctr, Beijing; 101312, China
[ 7 ] [Liu, Xuguo]Sinopec Beijing Research Institute of Chemical Industry, Yanshan Branch, Beijing; 102500, China
[ 8 ] [Wang, Zhan]Beijing Key Laboratory for Green Catalysis and Separation, Department of Chemistry and Chemical Engineering, Beijing University of Technology, Beijing; 100124, China
[ 9 ] [Gao, Shujuan]Beijing Key Laboratory for Green Catalysis and Separation, Department of Chemistry and Chemical Engineering, Beijing University of Technology, Beijing; 100124, China
[ 10 ] [Liu, Chao]College of Chemistry and Environmental Engineering, Anyang Institute of Technology, Anyang; 455000, China
[ 11 ] [Wang, Xi]Centre of Sino-Western Cultural Studies, School of Humanities and Social Sciences, Macao Polytechnic Institute, 999078, China

通讯作者信息：

王湛
[wang, zhan]beijing key laboratory for green catalysis and separation, department of chemistry and chemical engineering, beijing university of technology, beijing; 100124, china

电子邮件地址：

dwhx4077@163.com

查看成果更多字段

成果类型
所属机构

所有年份指定年份从至