THz　time　domain　spectrum　of　KH2PO4　crystal　in　the　range　from　0.2　to　1.6　THz,　the　far-infrared　spectrum　in　the　range　from　50-4000　cm(-1),　and　ultraviolet-visible-infrared　spectrum　in　the　range　from　200-2000　nm　were　measured　at　the　room　temperature.　The　energy　band　gap　Eg　of　KH2PO4　Crystal　is　5.91　eV.　There　is　a　wide　band　of　the　phonon　absorption　in　the　KDP　crystal.　The　values　of　the　absorption　coefficient　are　35-80　cm(-1)　in　the　range　from　0.2　to　205.5　THz.　The　end　of　the　low　frequency　of　the　optical　phonon　model　is　smaller　than　0.2　THz.　The　highest　frequency　upsilonLO　of　the　longitudinal　optical　phonon　model　LO　is　about　205.5　THz,　and　the　force　constant　K　of　H-O　ionic　chemical　bond　stretch　vibration　from　the　omegaLO　was　calculated　to　be　13.13　N　x　cm(-1).