The　single　phase　Ba1-xSrxTiO3　(x　=　0,　0.4,　0.8)　ceramic　compositions　were　fabricated　through　solid　state　(mixed　oxides)　method　calcined　at　850　degrees　C　and　sintered　at　1200　degrees　C　in　air.　The　XRD　patterns　revealed　the　single　phase　BaTiO3　composition　with　a　space　group　of　pm-3m.　The　shifting　of　the　(1　0　0)　XRD　peak　to　higher　2　theta　values　is　accredited　to　the　substitution　of　comparatively　smaller　ion　of　Sr2+　(1.4　angstrom)　for　larger　Ba2+　(1.6　angstrom)　ion　following　the　Braggs　diffraction　law　(2dsin　theta　=　m　lambda).　The　phase　transition　or　Curie　point　from　polar　ferroelectric　phase　to　non-polar　paraelectric　phase　of　Ba1-xSrxTiO3　was　reported　to　decrease　with　increasing　Sr2+　content　in　Ba1-xSrxTiO3　compositions.　The　value　of　the　dielectric　constant　decreased　with　increasing　the　content　of　Sr2+,　which　may　be　attributed　to　the　substitution　of　comparatively　smaller　ion　of　Sr2+　for　Ba2+　in　the　perovskite　structured　Ba1-xSrxTiO3.