In　this　study,　26　beam　specimens　were　subjected　to　flexural　loading　to　discuss　the　effects　of　cylinder　concrete　compressive　strength　(28　MPa,　37　MPa　and　43　MPa),　tensile　reinforcement　corrosion　(mass　loss　rates　of　2.1%　to　10.3%),　stirrups　corrosion　(mass　loss　rates　of　11.2%　to　26.3%),　and　loading　rate　(0.5　-　300　mm/min)　on　bond　capacities.　The　following　results　are　shown:　(1)　the　increase　of　concrete　strength　could　increase　the　bond　strength,　but　results　in　the　bond　stress　decreasing　more　rapidly　after　bond　failure;　(2)　the　existence　of　stirrups　could　not　significantly　improve　the　bond　strength　in　a　corrosive　environment,　since　a　wide　transverse　crack　width　(e.g.,　greater　than　1.0　mm)　on　concrete　would　be　induced　by　their　severe　corrosion;　(3)　the　increases　of　loading　rate　lead　to　about　34.8%　increases　in　the　bond　strength　while　decrease　the　peak　slip;　(4)　a　simplified　model　for　the　bond　stress-slip　curve,　incorporating　the　concrete　strength,　tensile　reinforcement　corrosion,　stirrups　corrosion　and　loading　rate,　is　proposed　and　validated.