摘要:

Solid-state additive manufacturing is a promising technology for production of high-strength aluminum alloy components. However, most solid-state AM technologies use thin foils or powder as feeding materials, limiting the deposition thickness of each layer and thus restricting deposition efficiency. This study is the first to utilize 2-mm-thick 5052-H32 aluminum alloy strips as feed material for a severe deformation-based friction rolling additive manufacturing (FRAM) method. In this study, the effect of process parameters such as rising height, transverse speed, and rotational speed, on the forming quality, microstructure, and mechanical properties of the resulting part were investigated. The results indicated that macroscopic forming defects can be avoided by selecting appropriate process parameters. A non-planar lamellar microstructure of fine and ultra-fine equiaxed grains densely embedded in each other was obtained without porosity or unbound defects; although the deposited material was not composed of completely equiaxed grains, the anisotropy of mechanical properties was small. The ultimate tensile strength and elon-gation in both the longitudinal and build directions of deposited material were higher than those of the raw feeding strips owing to the non-planar lamellar microstructure and grain refinement, with maximum values of 215 MPa and 32%, respectively. Through this microstructure analysis, the mechanism behind the formation of the lamellar micro-structure was elucidated. The concepts investigated here regarding defect-free, high strength, and high elongation lamellar materials by FRAM with thick strips as feeding material, provides a methodology for future preparation of laminated composites using FRAM.(c) 2023 The Author(s). Published by Elsevier B.V. This is an open access article under the CC BY-NC-ND license (http://creativecommons.org/licenses/by-nc-nd/4.0/).

关键词:

Mechanical properties Severe deformation Aluminum alloys Additive manufacturing Microstructure

作者机构:

  • [ 1 ] [Xie, Ruishan]Beijing Univ Technol, Fac Mat & Mfg, Beijing 100124, Peoples R China
  • [ 2 ] [Shi, Yanchao]Beijing Univ Technol, Fac Mat & Mfg, Beijing 100124, Peoples R China
  • [ 3 ] [Hou, Run]Beijing Univ Technol, Fac Mat & Mfg, Beijing 100124, Peoples R China
  • [ 4 ] [Liu, Haibin]Beijing Univ Technol, Fac Mat & Mfg, Beijing 100124, Peoples R China
  • [ 5 ] [Chen, Shujun]Beijing Univ Technol, Fac Mat & Mfg, Beijing 100124, Peoples R China

通讯作者信息:

电子邮件地址:

查看成果更多字段

相关关键词:

来源 :

JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T

ISSN: 2238-7854

年份: 2023

卷: 24

页码: 3788-3801

6 . 4 0 0

JCR@2022

被引次数:

WoS核心集被引频次: 14

SCOPUS被引频次: 13

ESI高被引论文在榜: 0 展开所有

万方被引频次:

中文被引频次:

近30日浏览量: 2

归属院系:

在线人数/总访问数:424/4965092
地址:北京工业大学图书馆(北京市朝阳区平乐园100号 邮编:100124) 联系我们:010-67392185
版权所有:北京工业大学图书馆 站点建设与维护:北京爱琴海乐之技术有限公司