Wang, Can (Wang, Can.) | He, Dingyong (He, Dingyong.) | He, Chengxing (He, Chengxing.) | Han, Feiyang (Han, Feiyang.) | Li, Jingchuan (Li, Jingchuan.) | Cui, Li (Cui, Li.) (学者:崔丽)

收录:

EI Scopus SCIE

摘要:

In this work, heat treatments were performed on autogenously laser welding of laser powder bed fusion (LPBF) AlSi10Mg alloys to improve mechanical properties of welded joints. After welding, the welded joint was heat treated by direct aging (DA) and solution heat treatment and artificial aging (T6) treatment. The porosity, microstructure and mechanical performance of the welded joints after DA and T6 treatments were investigated and compared with the as-welded joint. Results show that the microhardness of weld metal (WM) has been increased to over 93.5 HV0.1 after DA treatment, while the microhardness in the T6 welded joint is reduced to 77.0 HV0.1, from 82.0 HV0.1 in the as-welded joint. The ultimate tensile strength (UTS) of the DA treated joint reaches 276.5 MPa, showing an increase of 43.0% compared with as-welded joint. The DA heat treatment of the LPBF AlSi10Mg welded joints effectively improves the hardness and the UTS, which can be mainly attributable to the reduction of the hydrogen pores, the enhancing effect of solid solution strengthening coming from the Si element in the Al matrix and the dispersion strengthening of Si precipitation.

关键词:

Laser welding Microstructure T6 treatment LPBF AlSi10Mg alloy Direct aging treatment Mechanical properties

作者机构:

  • [ 1 ] [Wang, Can]Beijing Univ Technol, Coll Mat Sci & Engn, Beijing 100124, Peoples R China
  • [ 2 ] [He, Dingyong]Beijing Univ Technol, Coll Mat Sci & Engn, Beijing 100124, Peoples R China
  • [ 3 ] [Han, Feiyang]Beijing Univ Technol, Coll Mat Sci & Engn, Beijing 100124, Peoples R China
  • [ 4 ] [Li, Jingchuan]Beijing Univ Technol, Coll Mat Sci & Engn, Beijing 100124, Peoples R China
  • [ 5 ] [Cui, Li]Beijing Univ Technol, Coll Mat Sci & Engn, Beijing 100124, Peoples R China
  • [ 6 ] [He, Dingyong]Beijing Engn Res Ctr Ecomat & LCA, Beijing, Peoples R China
  • [ 7 ] [He, Chengxing]Yale Univ, Sch Engn & Appl Sci, Dept Chem & Environm Engn, New Haven, CT 06520 USA
  • [ 8 ] [He, Chengxing]Yale Univ, Energy Sci Inst, West Haven, CT 06516 USA

通讯作者信息:

  • 崔丽

    [Cui, Li]Beijing Univ Technol, Coll Mat Sci & Engn, Beijing 100124, Peoples R China

电子邮件地址:

查看成果更多字段

相关关键词:

相关文章:

来源 :

MATERIALS TODAY COMMUNICATIONS

年份: 2024

卷: 38

3 . 8 0 0

JCR@2022

被引次数:

WoS核心集被引频次:

SCOPUS被引频次: 11

ESI高被引论文在榜: 0 展开所有

万方被引频次:

中文被引频次:

近30日浏览量: 0

归属院系:

在线人数/总访问数:495/4958962
地址:北京工业大学图书馆(北京市朝阳区平乐园100号 邮编:100124) 联系我们:010-67392185
版权所有:北京工业大学图书馆 站点建设与维护:北京爱琴海乐之技术有限公司