Three　types　of　Ni8W/Ni12W/Ni8W　composite　substrates　with　strong　cube　texture,　high　yield　strength,　and　low　magnetization　were　produced　by　heavy　cold　rolling　and　annealing　processes.　The　three　types　of　composite　substrates　have　the　same　thickness,　but　the　ratios　of　thickness　between　Ni-8　at%W　and　Ni-12　at%W　layer　are　different.　The　contents　of　tungsten　exceed　9.3　at%,　10　at%,　and　10.3　at%　in　the　three　types　of　obtained　substrates.　The　presence　of　Ni　alloys　with　higher　W　content　in　the　Ni-12　at%W　of　the　three　composite　substrates　strongly　enhanced　the　mechanical　properties　with　about　290,　300　and　315　MPa　respectively,　and　decreased　the　ferromagnetic　behavior　of　the　whole　substrates.　Additionally,　it　was　found　that　an　area　that　enhances　cubic　nucleation　and　growth　in　the　Ni8W　layer　of　composite　substrates.