A facile 'one-pot' strategy was reported to synthesize a mesostructured Co/ordered mesoporous carbon (OMC) composite associated with a direct carbonization process from resol, cobalt oxalate and triblock copolymer F127. The obtained materials were investigated by X-ray diffraction (XRD), transmission electron microscopy (TEM), N2 adsorption-desorption and magnetometer measurements. The results show that the mesoporous composites with a low Co content possess an order 2-D hexagonal (p6mm) structure. With the increase of Co content, the order structure of the Co/OMC was gradually broken down. The surface area and pore volume of magnetic OMC will increase with a low Co conten, but they will decrease with the continued increase of the Co content. The cobalt-containing carbons exhibit soft ferromagnetic behavior at ambient temperatures and the magnetization parameters can be adjusted by the content of cobalt.