Preparation and hydrophilicity of mesoporous TiO2 thin films - 文章详情页

作者：

Li, Hui (Li, Hui.) | Wang, Jin-Shu (Wang, Jin-Shu.) (学者：王金淑) | Li, Hong-Yi (Li, Hong-Yi.) (学者：李洪义) | Zou, Chen (Zou, Chen.)

收录：

EI Scopus PKU CSCD

摘要：

Using　triblock　copolymer　Pluronic　F127(EO106PO70EO106)　as　the　templating　agent　and　Ti(OBun)4　as　the　inorganic　precursor,　mesostructured　TiO2　thin　films　were　prepared　through　sol-gel　combined　with　evaporation-induced　self-assembly　(EISA).　The　obtained　mesoporous　TiO2　films　have　uniform　mesopores　and　are　free　of　cracks　on　the　surfaces.　The　measurement　results　indicated　that　changing　the　weight　ratio　of　templating　agent　to　inorganic　precursor　could　adjust　the　pore　size　of　the　mesoporous　TiO2　thin　films.　When　the　weight　ratio　of　F127/Ti(OBun)4　varied　from　0.1　to　0.5,　the　pore　size　of　mesoporous　TiO2　films　calcined　at　500°C　changed　from　5.4　nm　to　9.1　nm.　The　obtained　mesoporous　TiO2　thin　films　exhibit　good　hydrophilicity.

关键词：

Mesoporous materials Hydrophilicity Thin films Self assembly Pore size Sol-gels Film preparation Titanium dioxide Fluorine compounds

作者机构：

[ 1 ] [Li, Hui]School of Materials Science and Engineering, Beijing University of Technology, Beijing 100124, China
[ 2 ] [Wang, Jin-Shu]School of Materials Science and Engineering, Beijing University of Technology, Beijing 100124, China
[ 3 ] [Li, Hong-Yi]School of Materials Science and Engineering, Beijing University of Technology, Beijing 100124, China
[ 4 ] [Zou, Chen]School of Materials Science and Engineering, Beijing University of Technology, Beijing 100124, China

通讯作者信息：

电子邮件地址：

Wangjsh@bjut.edu.cn

查看成果更多字段

成果类型
所属机构

所有年份指定年份从至