Microstructure and properties of arc sprayed nanocrystalline coating - 文章详情页

作者：

Fu, Bin-You (Fu, Bin-You.) | He, Ding-Yong (He, Ding-Yong.) (学者：贺定勇) | Jiang, Jian-Min (Jiang, Jian-Min.) | Li, Xiao-Yan (Li, Xiao-Yan.)

收录：

EI Scopus PKU CSCD

摘要：

Coating　containing　amorphous　phase　on　a　mild　steel　substrate　was　prepared　by　arc　spraying　using　Fe-based　cored　wire　as　spraying　material,　and　then　the　coating　was　annealed　at　600　°C　for　1h　for　crystallization　of　the　coating.　The　microstructure　and　properties　of　the　coating　was　investigated　by　means　of　XRD,　differential　thermal　analysis,　transmission　electron　microscopy　and　wear　test.　The　results　show　that　the　coating　exhibits　the　typical　lamellar　structure　with　little　pores.　The　grain　size　of　the　coating　is　10~40　nm.　Microhardness　of　the　coating　is　about　1143　HV0.1,　and　the　wear　resistance　of　the　nano-coating　is　five　times　better　than　that　of　3Cr13　coating.

关键词：

Crystallites X ray diffraction Microstructure Coatings Scanning electron microscopy Thermoanalysis Transmission electron microscopy Wear resistance Carbon steel Cavity resonators

作者机构：

[ 1 ] [Fu, Bin-You]College of Materials Science and Engineering, Beijing University of Technology, Beijing 100124, China
[ 2 ] [Fu, Bin-You]Beijing Jinlunkuntian Special Machine Co Ltd, Beijing 100083, China
[ 3 ] [He, Ding-Yong]College of Materials Science and Engineering, Beijing University of Technology, Beijing 100124, China
[ 4 ] [Jiang, Jian-Min]College of Materials Science and Engineering, Beijing University of Technology, Beijing 100124, China
[ 5 ] [Li, Xiao-Yan]College of Materials Science and Engineering, Beijing University of Technology, Beijing 100124, China

通讯作者信息：

电子邮件地址：

binyou@emails.bjut.edu.cn

查看成果更多字段

成果类型
所属机构

所有年份指定年份从至