Mesoporous　tungsten　trioxide　(WO3)　and　nickel　oxide　(NiO)　electrochromic　(EC)　thin　films　have　been　fabricated　by　sol-gel　method　with　assistant　of　tri-block　copolymer　[PEO132PEO50PEO132]　(F108).　By　controlling　weight　ratio　of　F108　and　calcination　temperatures,　uniform　and　transparent　mesoporous　films　are　fabricated.　Both　WO3　and　NiO　films　are　comprised　by　nanoparticles　with　diameters　of　ca.10　nm,　mesopores　with　pore　size　of　approximately　6　nm　are　distributed　in　the　films.　The　thickness　of　the　films　are　ca.　400　nm.　The　as-prepared　films　have　ultra-fast　switching　time　during　EC　redox　reactions.　Applied　with　positive　and　negative　voltages　of　40　s　respectively,　the　coloration/bleaching　time　of　WO3　and　NiO　films　are　5.7　s/2.3　s　and　0.9　s/3.8　s,　which　is　faster　than　that　of　comparative　EC　films　fabricated　by　sol-gel　method　without　F108　(coloration/bleaching　time　of　WO3　and　NiO　films　are　17.5　s/14.5　s　and　13.6　s/4.9　s)　and　EC　films　fabricated　by　magnetron　sputtering　method　(coloration/bleaching　time　of　WO3　and　NiO　films　are　29.4　s/21.3　s　and　9.6　s/7.5　s).　Quasi-solid　state　electrochromic　device　assembled　with　mesoporous　WO3　and　NiO　thin　films　has　excellent　EC　performance,　such　as　fast　switching　speed　(3.2/1.1　s　for　coloration/bleaching　time),　large　optical　modulation　of　about　45%　(at　600　nm),　high　coloration　efficiency　(130.8　cm(2)/C　at　the　wavelength　of　600　nm)　and　good　cycle　stability.　These　excellent　properties　are　derived　from　mesoporous　channels　in　the　films.　For　the　mesoporous　channels　can　shorten　the　diffusion　paths　and　make　it　easier　for　ions　to　transport　in　films.