Lead ferrite niobate perovskite fine powders prepared by coprecipitation method - 文章详情页

作者：

收录：

EI Scopus PKU CSCD

摘要：

Fine　powders　of　pure　perovskite　Pb(Fe1/2Nb1/2)O3　(PFN)　were　prepared　successfully　by　the　coprecipitation　method　and　using　the　raw　material　of　Nb2O5　changed　into　a　water-soluble　species　through　the　chemical　chelation　as　the　Nb　source.　Aqueous　ammonia　was　used　to　modulate　the　pH　of　the　solution　to　realize　the　simultaneous　precipitations　of　hydroxides　of　Nb5+,　Fe3+,　and　Pb2+　ions.　The　experiment　results　show　that　the　perovskite　phase　occurs　at　a　low　temperature　of　400°C　in　the　calcination　of　the　precipitation　product.　X-ray　diffraction　and　Raman　scattering　spectra　results　show　that　pure　perovskite　PFN　powder　was　synthesized　at　800°C.　Scanning　electron　microscopy　observation　shows　that　the　powder　has　a　cube-like　shape　and　nanoscale　grain　size　of　300-500　nm.

关键词：

Chelation Perovskite pH Powders Precipitation (chemical) Raman scattering Raw materials Scanning electron microscopy X ray diffraction analysis

作者机构：

[ 1 ] [Tang, Jianlan]College of Materials Science and Engineering, Beijing University of Technology, Beijing 100022, China
[ 2 ] [Zhu, Mankang]College of Materials Science and Engineering, Beijing University of Technology, Beijing 100022, China
[ 3 ] [Zhong, Tao]College of Materials Science and Engineering, Beijing University of Technology, Beijing 100022, China
[ 4 ] [Hou, Yudong]College of Materials Science and Engineering, Beijing University of Technology, Beijing 100022, China
[ 5 ] [Wang, Hao]College of Materials Science and Engineering, Beijing University of Technology, Beijing 100022, China
[ 6 ] [Yan, Hui]College of Materials Science and Engineering, Beijing University of Technology, Beijing 100022, China

通讯作者信息：

电子邮件地址：

查看成果更多字段

成果类型
所属机构

所有年份指定年份从至