Phase transformation in ξ-Al-Ni-Rh approximant phase induced by electron irradiation by in-situ TEM - 文章详情页

作者：

Zhai, Yadi (Zhai, Yadi.) | Chen, Yanhui (Chen, Yanhui.)

收录：

EI Scopus

摘要：

Electron　beam　irradiation　induced　phase　transition　processes　were　studied　on　crystalline　approximant　phase　ξ-Al-Ni-Rh　in　Al75Ni15Rh10　alloys.　Approximant　phase　to　amorphous　transition　phase　occurred　under　different　density　of　electron　beam　irradiation.　Phase　transition　and　separation　occurred　in　a　comparatively　lower　density　of　electron　beam　due　to　defects　modulation　and　defects　play　an　important　role　in　this　process.　Higher　density　electron　beam　induces　hollow　holes　with　amorphous　phase　in　the　rim　of　the　hole　in　the　sample　and　face　centered　structure　transition　phase　with　parameter　of　2.2　Å　appears　between　the　amorphous　phase　and　ξ-phase.　The　appearance　of　the　face　centered　structure　indicates　that　it　is　the　most　possible　shortest-range　order　in　amorphous　phase.　©　2020　Institute　of　Physics　Publishing.　All　rights　reserved.

关键词：

Electron beams Nickel metallography Rhodium metallography Ternary alloys Electrons Aluminum metallography Defects Nickel alloys Nanocrystalline materials Electron irradiation Aluminum alloys Rhodium alloys

作者机构：

[ 1 ] [Zhai, Yadi]Institute of Microstructure and Properties of Advanced Materials, Beijing University of Technology, No. 100 Pingle Yuan, Chaoyang District, Beijing; 100124, China
[ 2 ] [Chen, Yanhui]Institute of Microstructure and Properties of Advanced Materials, Beijing University of Technology, No. 100 Pingle Yuan, Chaoyang District, Beijing; 100124, China

通讯作者信息：

[chen, yanhui]institute of microstructure and properties of advanced materials, beijing university of technology, no. 100 pingle yuan, chaoyang district, beijing; 100124, china

电子邮件地址：

yhchen@bjut.edu.cn

查看成果更多字段

成果类型
所属机构

所有年份指定年份从至