Liang, Yueying (Liang, Yueying.) | Huang, Hui (Huang, Hui.) (学者:黄晖) | Wu, Xiaolan (Wu, Xiaolan.) | Wen, Shengping (Wen, Shengping.) | Gao, Kunyuan (Gao, Kunyuan.) (学者:高坤元) | Nie, Zuoren (Nie, Zuoren.) (学者:聂祚仁) | Li, Hongmei (Li, Hongmei.)

收录:

EI Scopus

摘要:

The mechanical properties and corrosion properties of 5E61 alloy cold-rolled sheet were studied under different stabilization annealing processes. The microstructure after alloy stabilization annealing was observed by optical microscopy (OM), scanning electron microscopy (SEM) and transmission electron microscopy (TEM), and the cold-rolled sheet stabilization process window was obtained. The results show that the 5E61 alloy has good corrosion resistance under different stabilization annealing processes; High strength and good corrosion resistance can be achieved in a short time in a higher stabilizing annealing temperature range; while after treatment in the lower stabilized annealing temperature range, the results show that the corrosion resistance is good under long-term annealing conditions and high mechanical properties are obtained, thereby the optimization of the stabilization process was carried out. © 2019, Springer Nature Singapore Pte Ltd.

关键词:

Aluminum alloys Annealing Cold rolling Corrosion resistance Corrosion resistant alloys Corrosive effects High resolution transmission electron microscopy High strength alloys Magnesium alloys Mechanical properties Metal cladding Scanning electron microscopy Stabilization Transmission electron microscopy

作者机构:

  • [ 1 ] [Liang, Yueying]School of Materials Science and Engineering, Beijing University of Technology, Beijing; 100124, China
  • [ 2 ] [Huang, Hui]School of Materials Science and Engineering, Beijing University of Technology, Beijing; 100124, China
  • [ 3 ] [Wu, Xiaolan]School of Materials Science and Engineering, Beijing University of Technology, Beijing; 100124, China
  • [ 4 ] [Wen, Shengping]School of Materials Science and Engineering, Beijing University of Technology, Beijing; 100124, China
  • [ 5 ] [Gao, Kunyuan]School of Materials Science and Engineering, Beijing University of Technology, Beijing; 100124, China
  • [ 6 ] [Nie, Zuoren]School of Materials Science and Engineering, Beijing University of Technology, Beijing; 100124, China
  • [ 7 ] [Li, Hongmei]School of Materials Science and Engineering, Beijing University of Technology, Beijing; 100124, China

通讯作者信息:

  • [liang, yueying]school of materials science and engineering, beijing university of technology, beijing; 100124, china

电子邮件地址:

查看成果更多字段

相关关键词:

相关文章:

来源 :

ISSN: 0930-8989

年份: 2019

卷: 217

页码: 93-104

语种: 英文

被引次数:

WoS核心集被引频次: 0

SCOPUS被引频次:

ESI高被引论文在榜: 0 展开所有

万方被引频次:

中文被引频次:

近30日浏览量: 1

在线人数/总访问数:136/3603119
地址:北京工业大学图书馆(北京市朝阳区平乐园100号 邮编:100124) 联系我们:010-67392185
版权所有:北京工业大学图书馆 站点建设与维护:北京爱琴海乐之技术有限公司