作者:

Cui, Su Ping (Cui, Su Ping.) (学者:崔素萍) | Wang, Xue Li (Wang, Xue Li.) | Wang, Jian Feng (Wang, Jian Feng.) | Liu, Hui (Liu, Hui.)

收录:

EI Scopus

摘要:

Through the XRD and XRF analysis of the converter steel slag, we can identify the chemical components and the mineral phase and ensure the extraction method of RO phase from steel slag. The possibility of the extraction of silicate phase from steel slag with Salicylic acid ethanol (SAE) solution was studied firstly. Then, the effect of dissolution temperature of steel slag, dissolution time of the samples, concentration of salicylic acid and specific surface area of steel slag on the extraction mass of silicate phase were analyzed by orthogonal experiment, and the optimum experiment conditions of the extraction of silicate phase from steel slag with SAE solution were concluded. Finally, the RO phase was obtained by the extraction and separation of the intermediate phase from steel slag using potassium hydroxide-sucrose (KOSH) solution. The effect of extraction was determined by detecting the chemical and mineral composition of the extracted residue with XRD and XRF. The results show that the SAE solution can be used to extract the silicate phase from steel slag and the best extraction conditions were 40 degrees of dissolution temperature, 3 h of solution time, salicylic acid concentration 0.2 g/ml and the specific surface area of steel slag 600 m2/kg. Then the intermediate phases (mainly C2F) from steel slag were extracted by KOSH solution, which can get a relatively pure RO phase. The experiment provides a basis for further exploring the cause of the difference in activity of RO phase and improving the utilization ratio of steel slag. © 2017 Trans Tech Publications, Switzerland.

关键词:

Slags Specific surface area Salicylic acid Potassium hydroxide Silicates Extraction X ray diffraction Chemical analysis Dissolution

作者机构:

  • [ 1 ] [Cui, Su Ping]Department of Material Science and Engineering, Beijing University of Technology, China
  • [ 2 ] [Wang, Xue Li]Department of Material Science and Engineering, Beijing University of Technology, China
  • [ 3 ] [Wang, Jian Feng]Department of Material Science and Engineering, Beijing University of Technology, China
  • [ 4 ] [Liu, Hui]Department of Material Science and Engineering, Beijing University of Technology, China

通讯作者信息:

电子邮件地址:

查看成果更多字段

相关关键词:

相关文章:

来源 :

ISSN: 0255-5476

年份: 2017

卷: 898 MSF

页码: 2470-2475

语种: 英文

被引次数:

WoS核心集被引频次:

SCOPUS被引频次: 5

ESI高被引论文在榜: 0 展开所有

万方被引频次:

中文被引频次:

近30日浏览量: 1

在线人数/总访问数:547/4955906
地址:北京工业大学图书馆(北京市朝阳区平乐园100号 邮编:100124) 联系我们:010-67392185
版权所有:北京工业大学图书馆 站点建设与维护:北京爱琴海乐之技术有限公司