The　unique　physical　properties　of　the　(1-x)K0.5Na　0.5NbO3-xLiNbO3　(KNN-LN)　ceramics　prepared　by　laser　sintering　were　studied　by　XRD　and　Raman　scattering　analysis.　The　larger　substitution　of　Li+　leads　to　the　composition　x　of　the　optimized　piezoelectric　properties　(d33=65　∼　105　pC/N　and　Tc=　400　∼　440　°C)　is　down　to　x　=　0.04　from　0.06.　Textured　structure　due　to　strictly　heating　directivity　of　laser　irradiation　resulted　in　fine　ferroelectric　properties　of　remnant　polarization　and　coercive　field　are　22.7　μC/cm　2　and　16.1　kV/cm.　The　phase　transition　between　tetragonal　and　orthorhombic　phases　(TO-T)　shifting　∼　0°C　from　room　is　beneficial　for　the　increasing　of　temperature　stability　of　the　ceramics　in　application.　It　is　shown　that　laser　sintering　should　be　one　of　promising　methods　in　preparation　of　functional　ceramics　with　applicable　physical　properties.